High sealing gaskets

ABSTRACT

A gasket having two opposed faces and an edge disposed therebetween is given a wide coating on the edge. The coating is sufficiently wide so that it goes from corner to corner on the edge and protrudes past the corner on at least one side of the gasket in a direction perpendicular to a facial plane of the gasket. The coating protrudes in an amount effective to give the gasket a sealing ability which is better than the sealing ability of the same gasket if it had a coating merely extending from corner to corner without protruding.

BACKGROUND OF THE INVENTION

Field of the Invention

This invention relates to gasket sheets which have good sealingproperties even at low flange pressures. More particularly, the presentinvention provides a gasket which can be used to seal fluids. Gaskets ofthe present invention, placed in a flange and having to seal againstfluids, can seal against fluid leaks both going through the gasket sheetinternally and across the gasket face.

Gasket sheets are used to seal fluids in engines. A number of solutionshave been employed in order to obtain good sealability (sealing ability)in the gaskets.

Beading on the face of the gasket is known. Such beading is a raisedarea put on the face; this beading, however, does not extend past theedge and further does not extend onto the edge. Such beading is used toenhance sealing.

One gasket material which can be used to give a good seal at hightemperatures is described in U.S. Pat. No. 5,240,766. This referencedescribes a gasket sheet material having fiber, filler, and binder.According to the reference, the filler component provides desirablesealability.

Another reference which describes gasket sheet materials is U.S. Pat.No. 5,536,565. This reference describes a gasket sheet material withfiber and filler. The filler component must include a gel-formingmineral. This filler gives the gasket good sealing properties,especially against polar liquids.

In spite of the wide use of gaskets to obtain a seal against fluids inengines, obtaining a good seal continues to be a problem in gasket sheetmaterials. Many gaskets do not seal well at low flange pressures. Othergaskets are given particular coatings in order to obtain a gasket sheetwhich will seal well. Unfortunately, such coatings are then responsiblefor the gasket having poor compression failure resistance.

The gaskets described herein provide good sealing ability even at lowflange pressures. In some embodiments the gasket is not coated or hasonly a limited amount of a coating given in order to obtain goodsealability, thus allowing the gasket to also be compression failureresistant.

SUMMARY OF THE INVENTION

A gasket sheet comprising two opposed faces, and an aperture with agasket sheet edge (also called the aperture's edge or the aperture'sgasket sheet edge) which is substantially perpendicular to the opposedfaces. The sheet edge further has at least one body which forms abarrier or dam to retard fluid from going from the aperture, past theedge and across a face of the gasket. The barrier can protrude from theedge or from the gasket face. When the barrier protrudes from the edgeit gets wider in a direction perpendicular to a facial plane of thegasket, and it protrudes past a corner plane at some point between thesheet edge and the aperture. The barrier is sufficiently wide to retardthe flow of fluid from the aperture across the face of the gasket, thusthe barrier protrudes a sufficient distance past the corner of thegasket sheet edge to be effective to give the gasket a better sealingability than the gasket would have if the barrier stopped at a point ina plane going through the corner of the edge (stopped at the cornerbetween the face and the edge).

In most embodiments of this invention the barrier is formed by a coatingthat is wider than the thickness of the aperture's gasket sheet edge,measuring the width of the coating going in a direction parallel to thesheet edge from one of the corners between the edge and the face throughthe other corner between the edge and the other face. The coating, atthe edge, thus being sufficiently wide to protrude past at least one ofsaid corners in a direction parallel to the surface of the sheet edge.The coating on the edge of the gasket sheet at the aperture goes beyondone of said corners in an amount sufficient to give the gasket a bettersealing ability than the gasket would have if the coating was only aswide as the thickness of the gasket sheet edge and thus stopped at bothcorners. The coating, however, does not necessarily lap around thecorner onto the face of the gasket, although optionally, it can.

The coating on the sheet edge, going beyond at least one of the cornerslaying between a face and the aperture's

gasket sheet edge (where the edge meets a gasket face), is hereinreferred to as a "wide edge coating" or a "protruding coating". Thecorner is located at each side of the edge where it abuts the face, atthe point between the face and the edge; this point can be identifiedeasily as the point where the cut, frequently porous edge ends and theless porous, non-cut face of the gasket begins.

In some embodiments the gasket is given a protruding coating on thesheet edge which is around the outside of the gasket (coating C). Thisis a secondary sealing position which seals the fluid from leaking pastthe gasket and outside of the flange, and as such it is less preferredthan the coatings on the aperture's edge which seals the gasket wherethe gasket is first and primarily exposed to fluid (giving a primaryseal). The edge coating around the perimeter of the gasket (coating C),must protrude past at least one corner of the edge of the gasket sheet,and preferably, in embodiments where the facial plane does not gothrough the corner of the gasket edge, the coating protrudes past thefacial plane.

The protruding coating, given to the gasket, may extend onto either orboth faces, and may extend so far as to completely cover one or bothfaces of the gasket except that the coating must protrude to provide thebarrier, and not be a level coating over the gasket. When the edgecoating sticks up past the corner plane or facial plane at an edge, thecoating provides a dam to retard fluids from going from the aperturepast the edge and out onto the gasket face between the face and aflange; where the edge is a perimeter edge the coating protrusion willstop fluids from going past the gasket out of the flange.

Furthermore, a completely coated gasket can take advantage of thesealing ability provided by the instant invention, although in someembodiments, to preserve compression failure resistance the amount ofcoating is preferably limited to cover only a portion of the gasket, therest of the gasket being left uncoated. In such embodiments it ispreferred to use a wide edge-coating to seal off the aperture's gasketsheet edge to fluids that go through the gasket itself. Preferably, topreserve compression failure resistance a coating will cover up to about50% of the gasket, and even more preferably it is limited to cover amaximum of about 30% of the gasket. In another preferred embodimentthere is no coating on either face of the gasket so that the gasket hasoptimized compression failure resistance.

Compression failure resistance is the ability of a gasket structure towithstand pressure without deforming the gasket to the point of failure.The crush test is an industry accepted measurement of compressionfailure resistance. The degree of compression failure resistance that agasket must have is typically set by the load that it will experience ina particular application or in a specific flange.

Suitably, the coating on the edge covers all of the portions of the edgewhich must be coated in order to give the gasket a good sealing ability.It may not be necessary, for example, to have the coating on the edge atbolt areas, or at non-porous portions of the edge. The edge is coated toallow the gasket to provide a better seal. Acceptable embodimentsinclude instances where the coating covers major portions of the edge.The gasket sheet edge can, thus be coated in an effective amount toachieve a substantial sealing of the gasket along the edge of theaperture. The edge, for example, can be coated up to about 75% of theaperture's gasket edge. Such embodiments can be used for good sealingability, where the very best sealing ability, obtained from coating theentire edge of the gasket does not have to be used. Preferably, however,the entire edge of the aperture is coated.

BRIEF DESCRIPTION OF THE DRAWINGS

The file of this patent contains drawings of FIGS. 1-3 executed incolor. Copies of this patent, with color drawings, will be provided bythe Patent and Trademark Office upon request and payment of thenecessary fee.

FIG. 1 is a color photograph illustrating a cross-sectional view of agasket with an aperture having a coated edge in accordance with thepresent invention.

FIG. 2 is a color photogrpah illustrating another example of across-sectional view of a gasket, which has an aperture with a coatededge in accordance with the present invention.

FIG. 3 is a photograph illustrating yet another example of across-sectional view of a gasket having an aperture with a coatinggasket sheet edge in accordance with the present invention.

FIG. 4 is a schematic, cross-sectional view of a portion of a gaskethaving a coating on the gasket sheet edge.

FIG. 5 is a schematic, cross-sectional view of a gasket having a coatingon a gasket sheet edge.

FIG. 6 is a schematic, cross-sectional view of a gasket having a coatingon an aperture's gasket sheet edge.

FIG. 7 is a top view of a gasket having a coated edge and a portion ofthe face of the gasket also coated.

FIG. 8 is a cross-sectional view of the gasket of FIG. 7.

FIG. 9 is a cross-sectional view of the gasket having a coating on itsedge.

FIG. 10 is a cross-sectional view of a gasket, which illustrates andouter edge or perimeter of a gasket having a coating on the gasket sheetedge of an aperture.

DETAILED DESCRIPTION OF THE INVENTION

FIG. 1 is a photograph showing an enlargement of a cross-sectionalportion of a gasket with an aperture having a coated edge. A portion ofthe coated aperture's gasket sheet edge is shown in the cross-section;this sheet edge is substantially perpendicular to opposed, parallelplanes, one plane laying on each face of the gasket (a facial plane). Inthe photograph the gasket can be seen to have two faces which aresubstantially parallel. The corner between the coated sheet edge andface is seen in the photograph at the top and bottom of the gasketsheet. In a direction parallel to the coated edge of the gasket, thecoating is wider than the edge and goes past the corner of the coatededge to thus protrude past the corner on the edge. Moreover, in fact,the coating is sufficiently wide so that the coating itself protrudespast the facial plane on at least one side of the gasket. The coating isa silicone rubber coating.

FIG. 2 is a photograph showing an enlargement of the cross-section of aportion of a gasket which has an aperture with a coated edge. A portionof the coated gasket edge is shown. The coated edge of the gasket sheetis seen and is substantially perpendicular to each face and to theopposed, parallel, facial planes that lie along each of the gasket'ssubstantially parallel faces. In the photograph the corner between eachface of the gasket and the coated edge of the gasket sheet is seen atthe top and bottom of the gasket. In FIG. 2, going through the coatingin a direction parallel to the edge of the gasket in the direction goingfrom corner to corner, the coating is wider than the coated gasket sheetedge and in fact is sufficiently wide so that the coating itselfprotrudes past the corner on each side of the edge, and in thisembodiment the coating also protrudes past the facial plane on bothsides of the gasket. This gives the gasket a better sealing ability thanit would have if the coating was level with the gasket on each face. Itthus gives the gasket a barrier on the gasket sheet edge to retard theflow of fluids from the aperture across the face of the gasket sheet. Inthis embodiment the coating also extends out onto the gasket face oneach side of the gasket. The coating is an acrylic latex.

FIG. 3 is a photograph showing an enlargement of a cross-sectionalportion of a gasket having an aperture with a coated gasket sheet edge.The coated edge is substantially perpendicular to each gasket face andto each of the opposed, parallel, facial planes that contains eachgasket face. The photograph shows a portion of the coated edge on thegasket sheet. Also, the corner between each face and the coated gasketsheet edge is seen at the top and bottom of the gasket in thephotograph. In the direction from corner to corner parallel to thegasket sheet edge of the gasket, the coating is wider than the edge andgoes past each corner and, in fact, the coating is sufficiently wide sothat the coating itself goes past the facial plane on each side of thegasket. In this embodiment the coating does not extend out onto eitherone of the gasket faces. The coating on each side of the gasket getsgradually wider than the edge until the coating comes to a point. Theembodiment of this photograph provides a gasket with a sealing abilityranging from a good seal to a total seal and simultaneously provides thebest (most optimized) compression failure resistance since neither ofthe gasket's faces has any coating to seal the gasket. The coating is anacrylic latex.

FIG. 4 is a drawing of an enlarged cross-section of a portion of agasket having a coating on the gasket sheet edge (71), said edge beingsubstantially perpendicular to the opposed planes (34 and 35) containingthe gasket faces (15 and 30) and the coating, in a direction parallel tothe edge is sufficiently wide so that the coating goes past the planes(34 and 35) on both sides of the gasket. Here, plane 34 and 35 are botha facial plane and a corner plane (going through the corner between theface and the coated gasket edge). The coating, getting gradually largerin a direction going away from the gasket's edge (71), thus gives thecoating a tapering effect so that the surface of the coating forms aninclined plane up to its widest point. This forms a barrier against thepassage of fluids across the face of the gasket. This is a preferredembodiment of the present invention (also shown in FIG. 3).

FIG. 5 is a drawing of an enlarged cross-section of a portion of agasket having a coating on an aperture's gasket sheet edge (72), saidedge being substantially perpendicular to opposed faces (17 and 31). Thecoating (18) here is wide enough, in a direction parallel to the edge,to go past the corner of the gasket which is at the top of edge (72),and past the facial plane (54). Here, the facial plane (54) is not thesame as the corner plane (not indicated) which goes through the cornerof the edge.

FIG. 6 is a drawing of an enlarged cross-section of a portion of agasket having a coating on an aperture's gasket sheet edge (75). Theedge (or edge surface) is substantially perpendicular to opposed faces(24 and 32).

The coating (26) protrudes past "facial planes" or "corner planes"(37and 38) on both sides of the gasket. Here, the facial plane and thecorner plane are the same plane.

FIG. 7 is a drawing of a gasket (10) having a coated edge (12) and aportion of the face of the gasket is also coated (11).

FIG. 8, is a drawing of an enlarged cross-section of the gasket of FIG.7, as indicated. The coating (12) is indicated on the aperture's gasketsheet edge (76) and the extended portion (11) of the coating that lapsonto face (25) is also indicated. Facial, corner planes (39 and 65) areshown. The coating protrudes past the planes, going in a directionparallel to edge (76). In more preferred embodiments the coating willprotrude at least about 1 mil past that part of the coating that is onthe face of the gasket, as is shown, for example, by FIG. 2 and FIG. 8.In FIG. 2 the coating is seen to extend out onto the face of the gasket,but the coating from side to side in a direction parallel to the edge iswider than the distance from the surface of the coating passing throughthe gasket sheet and out to the surface of the coating on the otherside. In FIG. 8 the barrier against fluids extends over the faces (25)and (33). In FIG. 2 on each side of the gasket the barrier againstfluids rests on and inclines slightly over the gasket face.

FIG. 9 is a drawing of an enlarged cross-section of a portion of agasket having a coating (41) on the edge (77). The coating protrudespast the corner of the edge which lies between the face (40) and theedge (77), (thus going past the corner plane (41) but the coating doesnot extend past the facial plane (36). Such a coating, on one side ofthe gasket provides a barrier against fluids that might otherwise gofrom the aperture across the face (40) of the gasket, although thebarrier (dam) is not as high, i.e. not as far past the face (24) as thecoating of FIG. 6.

FIG. 10 is a drawing of an enlarged cross-section of a gasket whichshows the outer edge or perimeter (47) of a gasket having coating (48)on an gasket sheet edge (78) of an aperture. The gasket has beading (46)and face areas which are lower (49) than the facial plane; these areascan be made by embossing. The coating (48) goes past the plane (60)which is both a facial plane and a corner plane. Faces (44) and (45)both show areas made by embossing and beading; the extension of thefacial plane (60) is seen going through the gasket face, from one sideof the gasket, through the gasket to the other side. It can be notedthat the facial plane (60) contains the flat portions of the face (45)of the gasket and the corner between the coated edge (78) and the face(45).

A protruding coating is effective to retard or to stop the flow offluids across the face of any gasket which must seal against fluids. Thecoating does this by providing a dam on the edge of the gasket. This"dam" is the protruding portion of the edge coating and is a preferredbarrier to the fluid.

A soft gasket material can be given an edge seal on an aperture exposedto fluids and obtain a seal against the fluid. Surprisingly, there is noneed to change the composition of the sheet material for any significantimprovement in sealing ability. The edge coating delivers the seal.Surprisingly, in many cases there is no need for significant sealingability in the base sheet. Furthermore, a base sheet with the edge sealcan accommodate many different types of flanges without any change beingmade to the base sheet.

Any gasket material which seals against fluids can take advantage of thepresent invention. This includes coated or uncoated gaskets; soft gasketmaterials; and layered gaskets such as gaskets which have a compressibleor non-compressible core in between two layers or which have anincompressible substrate sheet on one side of the gasket. In embodimentswhere the gasket has more than one layer, a protruding coating on theedge of the aperture could be only on one layer. Preferably, however,the protruding coating would extend across the layers completely in adirection from one of the corners between a face and the edge to theother corner between the other face and the edge and would go beyond atleast one of the corners. Preferably the coating would penetrate andseal off any cracks present between the layers.

In some embodiments, the barrier extends in a direction perpendicular toat least one facial plane, past the corner between the gasket sheet edgeand the face. Some embodiments have a barrier on the edge coating wherethe coating extends over the edge. Preferably the gasket will havebarriers protruding past both corners of the aperture, such as in FIGS.6 and 8.

Some embodiments of the present invention, however, are ideally suitedand highly preferred for gaskets which are compressible and porous andwhich must also seal against fluids going through the gasket. In such acase, a wide edge-coating on an gasket sheet edge which covers the edgefrom corner to corner and past the corner; protruding past the cornerplane in a direction perpendicular to the facial plane, will give thegasket a better sealing ability, especially since it seals against twotypes of fluid flow; both through the gasket and across the gasket face.This is particularly true where the aperture has been cut in the gasket.The cut edge will have more pores than another surface which is not cuteven in porous and compressible gaskets. Coating the edge so that thecoating penetrates or closes off the pores will be effective to seal offthe pores to fluid which could seep through the gasket.

Soft gasket materials are preferred for use with the wide edge-coatingof the present invention. Many types of soft gasket materials comprisefiber and a binder; other types of soft gasket materials comprise abinder and a filler, such as, for example, rubber and cork. Many softgasket materials comprise fiber, binder, and filler. Such soft gasketmaterials have pores along the sheet edge where the aperture has beencut. These pores are detrimental to the sealing ability of the gasket.Thus, it is preferred to have an edge coating on the aperture's gasketsheet edge which will penetrate or at least close off the pores. In someembodiments the aperture is a bolt hole.

When the gasket sheet material comprises fiber and inder, in most cases,a filler is also present. The gasket sheet should have at least 1% bywt. of the binder and at east about 5% by wt. of the fiber. Filler canalso be added a t a minimum level of about 1%. Suitable ranges are fromabout 3 to about 40% by wt. of the binder, from about 5 to about 70% byweight (wt.) of the fiber, and from about 1 to about 92% by wt. of thefiller.

Preferred gaskets that can use the present edge seal are gaskets forintake manifolds, oil pan gaskets (sealing against oil); cover gasketssuch as a valve cover (which seals against oil) or an axle cover (whichseals against gear lubricant); and compressor gaskets which arefrequently exposed to refrigerants such as freon; a gas meter gasketwhich seals gas; a water pump gasket which seals against water andantifreeze; and a gasket for an industrial flange which will sealagainst steam and/or chemicals. The type of coating for each applicationis important to achieve preferred embodiments since some particulartypes of coatings will hold the particular fluid better than others.This wide edge sealing design has, in fact been found to be surprisinglysuited for sealing oil pans of diesel engines and for sealing vacuum inintake manifolds against air and fuel mixtures. Chloroprene polymer andacrylonitrile are the preferred coatings for embodiments with exposureto refrigerants; acrylic or acrylonitrile are the preferred coating forembodiments with exposure to oil or gear lubricant.

On each end of the aperture's gasket sheet edge there is a corner whichabuts a gasket face. Each corner can be considered to lie in twodifferent parallel, infinite planes (such as, for example, in FIG. 8having plane 39 and plane 65). The plane is a "facial plane" when itgoes through the substantially flat surface area of a gasket face. Thefacial plane thus contains the flat surface area of the gasket face.Generally, the edge of the gasket sheet around the aperture issubstantially perpendicular to the facial plane. A plane is a "cornerplane" when the infinite plane contains a corner between the face andthe edge. In some cases the facial plane does not go through the cornerso that there is both an infinite "facial plane" and an infinite "cornerplane" (such as in FIG. 5 which shows the facial plane (54)) and FIG. 9which shows corner plane (80) and facial plane (36). When the facialplane goes through the corner between the face and an aperture's gasket.sheet edge the plane is both a corner plane and a facial plane (a"corner, facial plane"). A coating which extends beyond the cornerexisting between the edge and the face will protrude past the cornerplane as does coating (41) of FIG. 9. The coating should protrude pastthe corner plane in order to provide the seal against fluids which wouldotherwise seep out onto the gasket face between the gasket face'ssurface and the flange.

In some preferred embodiments the coating protrudes past both a cornerplane and a facial plane (in embodiments where the facial plane does notgo through the corner of the aperture's gasket sheet edge). Suchembodiments provide an even better barrier against fluids from goingacross the face of the gasket, between the face and the flange.

The "edge thickness" is the distance on the edge from one corner whichlies between one face and the edge and the other corner which liesbetween the other face and the edge. In the present invention, to obtainsealing ability across the face of the gasket and through the gasket,the edge coating is wider than the edge thickness so that the edgecoating goes beyond a corner plane on at least one side of the gasket.

In most cases the facial plane and the corner plane will be the sameplane. In some cases, however, by using pressure, a facial area can beforced into a different plane than the rest of the face. When this isdone abutting an aperture, the corner between the face and the edge maybecome rounded and it may be more difficult to place the location of thecorner plane. In such cases the corner plane is easily located by notingthe point where the cut portion of the edge ends; this point is in thecorner plane. The cut portion of the edge typically contains more poresthan the surface of either gasket face and is also distinctive inappearance by showing a cross-section of the materials inside thegasket.

The coating portion on the gasket edge, such as in FIGS. 9, 10, 4, 6,and 3 can be referred to herein as coating A. FIGS. 2 and 8 showembodiments where coating A is on the gasket material's edge, and sincethe coating also overlaps onto the face of the gasket, it also has acoating B. Thus, where the coating extends to cover the gasket face, thecoating portion on the face can be referred to as coating B, such as isseen in FIG. 8 and FIG. 2; coating A is on the gasket edge. A coatinglike coating A which is on the outside perimeter of the gasket sheetedge is herein referred to as coating C. Where coating C extends overthe face of the gasket it is coating B. Preferably, coating A extendspast coating B, protruding past the surface of coating B at least about1 mil on at least one side of the gasket; more preferably coating Aprotrudes at least about 5 mils past coating B, and most preferablycoating A protrudes past coating B at least about 10 mils on at leastone side of the gasket. The preferred embodiments has coating Aprotruding past coating B on both sides of the gasket. Features wherecoating A extends past the gasket face at the corner of the edge (thusprotruding past the facial, corner plane), or where coating A extendspast coating B, can be referred to as a "lip formation" or a "lip". Thislip forms a dam or barrier against fluids on the aperture side of thecoating.

At least one edge, which is around an aperture and is substantiallyperpendicular to the substantially opposed faces can be given a wideedge-coating which goes past at least one corner of the edge (protrudingthrough the corner plane of that corner). In a direction from one of thecorners between a face and the edge past the other corner between theother face and the edge and parallel to the edge, the protrudingcoating, should be sufficiently wide to give the gasket a better sealingability than the gasket would have with a coating which just extendedfrom one of the corner planes to the other corner plane (merely touchingthe corner plane).

Suitably, in this direction, the aperture's gasket sheet edge has abarrier (such as a coating) that protrudes past the corner plane adistance of at least about one mil. A coating from corner to corner willthus be at least about 1 mil wider than the edge is thick. Furthermore,it has been found that an even wider barrier coating will give an evenbetter sealing ability. More preferably, therefore, the barrierprotrudes at least about 5 mils beyond one corner plane. Suitably, thebarrier ranges from about 1 to about 80 mils past the corner plane. Thewide edge-coating can thus protrude past either or both corner planes adistance of from about 1 to about 80 mils. A more preferred range isfrom about 5 to about 80 mils, still more preferably the coatingprotrudes a distance of from about 10 to about 80 mils past the cornerplane. Preferably, the wide edge-coating protrudes past at least onecorner plane a distance of at least about 10 mils, more preferably thewide coating extends past each corner plane a distance of at least about10 mils; gaskets with such coatings, in fact have been found to give aseal ranging from excellent to a total seal. This is true even withflange pressures of about 300 PSI or more, or about 25 PSI or more. Atotal seal is found where the coating will completely prevent fluidsfrom leaking past the aperture, across the face of the gasket and alsothrough the gasket sheet. To achieve such a seal it is preferred thatthe wide edge-coating protrudes past each corner plane a distance of atleast about 15 mils.

For a gasket giving a total seal it is also preferred that from the edgesurface, in a direction going into the aperture parallel to the facialplane and away from the edge, the coating on the edge gets graduallywider (as seen in FIGS. 2, 3, and 4) forming an inclined plane, until itcomes to the coating's widest point at some distance from the edge. Thedistance from the edge that the coating extends and reaches its widestpoint is not critical. Suitably, however, in such an embodiment, thecoating is at least one mil wider than the thickness of the gasket edge.Preferably the coating is at least 5 mils wider than the thickness ofthe gasket edge. It is preferred that a "lip" is formed, such as in FIG.6, or such as in FIGS. 2, 3, and 4 (where the lip resembles an inclinedplane and is formed by the coating getting gradually wider going awayfrom the aperture's gasket sheet edge).

In embodiments where a face has a facial plane that does not go througha corner between the face and a plane, it is optionally preferred tohave a barrier that protrudes beyond the facial plane. Suitably thebarrier will protrude past the plane in an amount effective to give abetter seal than the gasket would have if the barrier merely came up tothe facial plane but did not go past it. The coating can protrude atleast about 1 mil beyond such a facial plane; more preferably it extendsat least about 5 mils beyond such a facial plane and even morepreferably it extends at least about 10 mils beyond such a facial plane.Preferably, the barrier will go at least about 1 mil past at least onefacial plane; more preferably it will go at least about 5 mils past atleast one facial plane, and even more preferably the coating will go atleast about 10 mils past at least one facial plane; total seals havebeen achieved particularly when the coating protrudes at least about 15mils past the facial plane; in a preferred range the barrier will extendfrom about 5 to about 80 mils past at least one facial plane (includingembodiments where the facial plane lies above or outside the cornerplane on the face of the gasket as noted in FIG. 5 and FIG. 9). The morepreferred embodiments has the barrier in the form of a coating extendingbeyond the facial plane on both faces of the gasket.

The coating can be put on in any film-forming manner such as, forexample, dipping, melting or painting the exposed edge while protectingany gasket portions not to be coated. In one embodiment a coating can beput on an aperture edge (the edge of the gasket sheet) by placing aplurality of gasket sheets together so that a cavity is formed from theapertures of the plurality of gasket sheets, and then contacting theedge of each gasket sheet along the cavity with a coating material sothat the edges become coated in an amount effective to achieve asubstantial sealing of the gasket along the edge of the gasket sheet atthe aperture where the edge is coated.

The gaskets can be aligned and placed together so that they abut, or, insome of these embodiments it may be desired to place other sheets inbetween two or more of the gasket sheets. Such sheets in between thegaskets would be "spacers" to separate the gaskets from each other. Thespacer sheets will also have apertures, but the apertures can be wideror smaller than the apertures of the gaskets. When the spacer apertureis wider, a portion of the gasket sheet face is exposed, and the coatingmaterial can contact and coat the face where it is exposed around theaperture. When the spacer aperture is smaller the gasket sheets will beseparated from each other and less coating will overlap the corner ofthe edge onto the face of the sheet. Spacers can be coated to make thegasket coating material release easily. Spacers can also be used to formthe protruding coating on an edge. In other embodiments the spacers canbe configured to give the final wide edgecoating a different shapeparticularly where the coating protrudes past the corner plane.

However, even when the gasket sheets are placed together to form acavity from the apertures and the coating contacts the surface of thecavity, then separating the gaskets while the coating is viscous orelastic (before the coating cures or becomes hard) will stretch thecoating so that it becomes wider than the aperture's gasket sheet edge.When the coating has partially cured or when it is plastic and moldable,then separating the sheets can cause the oating on the edge to be morepointed and wider than the aperture's edge (this is shown by FIGS. 2 and3) forming an inclined plane. This technique is done easily andpreferably with acrylic latex.

In still other embodiments, some of the aperture's gasket sheet edge canbe protected from the coating material so that only a portion of eachedge of the gasket sheet at the aperture are contacted with the coatingmaterial. This can be useful where the edge is close to a bolt area.Where the edge is within, for example, 3.5 cm. (centimeters) of a bolt,it may be desired to preserve more compression resistance by not addingcoating even to the edge. The extra pressure added by the bolt will beeffective to give some added sealing ability to the gasket, so that itmay not be necessary or desired to completely coat the aperture's gasketsheet edge. To achieve such embodiments a spacer sheet is configured tocover the portion of the edge which is not to be coated. Where thegasket must seal against fluids that would go through the sheet of thegasket, however, the coating material should contact the edge portion tobe coated so that the coating material covers the edge going completelyfrom one corner to the other corner. A bolt area is an area near orunder the bolt where higher pressure is put on the gasket than on areasfurther away from the bolt.

Any vertical edge between the opposed faces of a gasket sheet materialcan be given a coating, including the edge which forms the outerperimeter of the gasket. The coating can be organic or inorganic. Whenthe vertical edge is one which encounters fluids during use, however, apolymer coating is particularly useful and preferred.

Optionally, a coating strip (coating B) can be put on one or both facescompletely around an aperture so that it abuts the edge perpendicular toeach face and also abuts or even joins with the coating on theaperture's gasket sheet edge (coating A). The coating strip can bebeneficially used where the flanges do not fit together tightly to forma fitted seal against fluids. If, for example, a flange is warped evenslightly so that it curves away from a planar (flat) surface, thecoating strip can be useful in providing a better seal against fluidleakages. For such applications, the coating strip will preferably beput around the aperture where fluids are encountered in use.

The coating on the aperture's gasket sheet edge (coating A) can overlaponto either or both faces, forming coating B. The overlap can extend adistance ranging from just a trace, less than 1 mil or can extend overthe entire gasket surface. The edge coating on the vertical edge can lapover onto either or both faces of the gasket (such as is shown, forexample, in FIG. 8). Preferably, the sealing coating can extend up toabout 1.5 cm. on the face of the gasket. More preferably, it extends amaximum of about 5 millimeters (mm) across the face of the gasket, andmost preferably it extends a maximum of about 1 mm; such embodiments arefor good compression resistance (minimizing coating on the gasketfaces).

Optionally, each gasket face or a portion thereof, can be given only arelease coating, and not any coating for sealing the gasket. This willgive the gasket more compression resistance. Release coatings, ingeneral do not substantially affect compression resistance. A releasecoating is normally less than 1 mil in thickness. The coatings to sealthe gasket, however, are heavier, thicker, and generally morepenetrating into the gasket and gasket pores than is a release coating;thus, the coatings for sealing ability are detrimental to compressionresistance and are thus limited in embodiments where it is important topreserve compression resistance.

It has been found that the thickness of the coating on the face of thegasket also will be detrimental to compression resistance. For thisreason therefore, it is preferred that the overlap of the edge coatingonto the face of the gasket is a maximum of about 11 mils thick in orderto preserve compression resistance.

When the release coating is to be used, for best performance, therelease coating does not penetrate the gasket structure. This will givethe gasket more compression failure resistance than if the releasecoating penetrated. A suitable release coating is a flouropolymercontaining polymer coating.

Practicality is the factor limiting the thickness of the coating on thevertical edge, that is thickness in both the direction parallel to thevertical edge and perpendicular to the vertical edge. Very smallthicknesses (going perpendicular to the edge) have been found to beeffective. Since a relatively thin coating is effective it will be costeffective to limit the thickness and width of the coating on thevertical edge of the gasket aperture.

The coating thickness, in the direction perpendicular to the verticaledge and parallel to the facial plane thus, is not critical. The coatingpreferably is a minimum of at least about 0.1 mm thick and preferablycan be up to about 2 mm thick. The coating on the vertical edge isintended to seal the gasket against fluids from going both through thegasket sheet edge and across the surface of at least one gasket face.The coating should have a minimum thickness needed to seal the gasketagainst fluids from going through the aperture's edge. Suitably thesealing coating on the edge of the soft gasket sheet should be at leastabout 1 mil in thickness (extending in a direction perpendicular to thevertical edge). Preferred embodiments will have a protruding edgeforming a barrier that goes beyond the corner plane a sufficientdistance to give the gasket a seal. against fluids from going across atleast one gasket face, and preferably across both faces.

Inorganic materials which can be used as a coating includes chemicallydelaminated vermiculite and mica coatings. Preferred coatings arepolymers. The polymer coatings can be used to form either coating A,coating B, and/or coating C. Polymer coatings include organic,inorganic, inorganic/organic hybrid polymers as well as filled polymers.Suitably the polymer coating materials are coatings selected from thegroup consisting of acrylic, acrylonitrile, polyvinylidene chloride,fluorosilicone, polyurethane, acrylonitrile butadiene rubber (NBR),fluoro polymers, hydrogenated NBR, silicone rubber coatings (both UVcurable and room temperature curable), styrene butadiene polymer,fluoroelastomer polymer, fluorosilicone polymer, acrylic-acrylonitrilepolymer, carboxylated acrylonitrile polymer, carboxylated styrenebutadiene polymer, chloroprene rubber polymer, ethylene propylene rubberpolymer, ethylene/vinyl acetate, epoxy, and mixtures thereof can beused. Any latex can be used. Also suitable as a coating are polymerpowders which are heated to melt them onto the surface of the gasket. Infact, any powder which can be fused can be used to seal and coat thegasket. Coatings A, B, and C can be made by different coatings or theycan be the same material.

EXAMPLES

Two identical annular gaskets were cut from a cellulose based papergasket sheet material. Each gasket formed a ring and had the followingmeasurements: Inner diameter 0.515 inches (distance from the center ofthe aperture to the inner edge of the ring), outer diameter 0.95 inches;ring width 0.2175 inches. The gaskets each had two substantially flat,opposed faces and each ring aperture had an edge that was substantiallyvertical and substantially perpendicular to each face. The edgethickness (also the gasket thickness) was measured at 32 mils thick.

The gasket ring for sample A was left completely uncoated as thecontrol. For sample B, an acrylic latex was used to coat the gasket ringsample on the inner vertical edge of the ring aperture. The coating wasput onto the aperture's gasket sheet edge so that the coating was widerthan the thickness of the aperture's edge (wider than the gasketthickness), and went past each corner of the inner, vertical edge byapproximately 27 mils on each side, measuring the coating at its widestpoint. The distance from the inner, vertical edge of the gasket to thesurface of the coating at the center of the gasket was measured at about0.9 mm. (millimeters). The coating on the edge of the gasket sheet atthe aperture was like the coating shown in a cross-sectional view inFIG. 4 and FIG. 3.

The gasket was tested in a cylinder which could be pressurized withnitrogen. The nitrogen pressure in the cylinder was brought up to 14 PSI(pounds per square inch), and the number of minutes which elapsed whilethe pressure decayed to 13 PSI was measured. Each gasket was placed inthe cylinder's flange and the flange was tightened. The test was done ona smooth flange measuring 18 RaMS (Ra is the average roughness value andthis is measured in micro-inches; MS indicates micro-inches). The flangewas tightened and the pressure level of the flange was measured inpounds per square inch (PSI).

Sample A for this test held the pressure only for 1.5 minutes andrequired a flange pressure of 2100 PSI. Sample B, the wide edge sealedgasket, delivered a total seal (pressure never decreased in thecylinder), and the flange pressure of the cylinder on the gasket ofsample B was only 300 PSI.

I claim:
 1. A sealing gasket comprising a sheet with two opposed,substantially parallel faces, said gasket further having an edge surfacedisposed between each face, said edge surface being around an aperture,said edge surface being substantially perpendicular to each face, theedge surface further having a sealing coating disposed thereon which iswider than the edge surface in a face to face direction parallel to theedge surface so that the coating protrudes at least about 1 mil beyondat least one face and extends past the face in a direction perpendicularto the face to provide a barrier against fluids, said coating furthercovering all portions of the edge in order to give the gasket a goodsealing ability, and said coating further being thick enough on the edgeto seal the gasket against fluids from going through the edge, furtherproviding that the sheet comprises fiber in a amount in the range offrom about 5 to about 70% by weight, filler in an amount in the range offrom about 1 to about 92% by weight, and binder in amount of from about3 to about 40% by weight, said sheet further being compressible andporous and the edge of the aperture having pores which are sealed off bythe coating on the edge, further providing that to preserve compressionfailure resistance less than about 50% of the gasket has a coating forsealing ability.
 2. The gasket of claim 1 wherein at least one facialplane goes through a corner that lies between the edge surface and aface.
 3. The gasket of claim 1 wherein no facial plane goes through acorner that lies between the edge surface and a face.
 4. The gasket ofclaim 1 where the coating is on only part of the edge.
 5. The gasket ofclaim 1 where the coating is on the entire edge surface.
 6. The gasketof claim 1 wherein the coating extends at least about 10 mils past bothfaces of the gasket.
 7. The gasket of claim 1 wherein the coating is apolymer.
 8. The gasket of claim 1 which is either an oil pan gasket,which must seal against oil or a cover gasket which must seal againstgear lubricant.
 9. The gasket of claim 1 which is a gasket for an intakemanifold.
 10. The gasket of claim 1 which is a compressor gasket. 11.The gasket of claim 1 which must seal against a refrigerant.
 12. Thegasket of claim 1 which is a gas meter gasket for sealing against gas.13. The gasket of claim 1 which is for an industrial flange to sealagainst steam and/or chemicals.
 14. The gasket of claim 1 in which thecoating on the edge surface is acrylic or acrylonitrile which sealsagainst either oil or gear lubricant.
 15. The gasket of claim 11 inwhich the coating on the edge surface is chloroprene polymer.
 16. Thegasket of claim 1 in which the coating is a coating material selectedfrom the group consisting of acrylic, acrylonitrile, polyvinylidenechloride, fluorosilicone, polyurethane, acrylonitrile butadiene rubber,fluoro polymers, hydrogenated NBR, silicone rubber coatings, styrenebutadiene polymer, fluoroelastomer polymer, fluorosilicone polymer,acrylic-acrylonitrile polymer, carboxylated acrylonitrile polymer,carboxylated styrene butadiene polymer, chloroprene rubber polymer,ethylene propylene rubber polymer, ethylene/vinyl acetate, epoxy, andmixtures thereof.
 17. The gasket of claim 1 wherein the coating extendspast each face.
 18. The gasket of claim 1 wherein the gasket further hasan outside edge surface disposed between each face, said outside edgesurface forming a perimeter around the gasket, said outside edge surfacebeing substantially perpendicular to each face, the outside edge surfacefurther having a coating disposed thereon which is wider than theoutside edge surface in a face to face direction parallel to the surfaceso that the coating protrudes at least about 1 mil beyond at least oneface and extends past the face in a direction perpendicular to the face.19. The gasket of claim 1 wherein the coating forms an inclined plane oneach side of the coating as a result of the coating on the edge gettinggradually wider in a direction substantially perpendicular to the edge,each inclined plane abutting each face of the gasket sheet.
 20. Thegasket of claim 1 having a release coating on at least a portion of thegasket sheet which has not been coated for sealing ability.
 21. Thegasket of claim 1 in which the coating extends a distance in the rangeof from about 5 to about 80 mils past each face.
 22. A gasket comprisinga sheet with two opposed, substantially parallel faces, said gasketfurther having an outside edge surface disposed between each face, saidoutside edge surface forming a perimeter around the gasket, said outsideedge surface being substantially perpendicular to each face, the outsideedge surface further having a coating disposed thereon which is widerthan the outside edge surface in a face to face direction parallel tothe surface so that the coating protrudes at least about 1 mil beyond atleast one face to form a barrier against fluids and extends past theface in a direction perpendicular to the face, said coating being thickenough on the edge to seal the edge against fluids said coating furthercovering all portions of the edge in order to give the gasket a goodsealing ability; further providing that the sheet comprises fiber in aamount in the range of from about 5 to about 70% by weight, filler in anamount in the range of from about 1 to about 92% by weight, and binderin amount of from about 3 to about 40% by weight, said sheet furtherbeing compressible and porous and the outside edge surface having porestherein which are sealed off by the coating on the edge, furtherproviding that that to preserve compression failure resistance less thanabout 50% of the gasket has a coating for sealing ability.
 23. Thegasket sheet of claim 22 wherein at least one facial plane goes througha corner that lies between the edge surface and a face.
 24. The gasketsheet of claim 23 where the coating extends past the corner of eachface.
 25. The gasket sheet of claim 24 where the coating is on theentire edge of the sheet.
 26. The gasket sheet of claim 22 wherein nofacial plane goes through a corner that lies between the edge surfaceand a face.
 27. The gasket sheet of claim 22 wherein the coating is apolymer.
 28. The gasket of claim 22 which is either an oil pan gasket,which must seal against oil, or is a cover gasket which must sealagainst gear lubricant.
 29. The gasket of claim 28 wherein the coatingis either an acrylic polymer or an acrylonitrile polymer.
 30. The gasketof claim 22 which is a compressor gasket.
 31. The gasket of claim 22which must seal against a refrigerant.
 32. The gasket of claim 31 inwhich the coating on the edge surface is chloroprene polymer.
 33. Thegasket of claim 22 which is a gas meter gasket for sealing against gas.34. The gasket of claim 22 which is for an industrial flange to sealagainst steam and/or chemicals.
 35. The gasket of claim 22 wherein thecoating is a coating material selected from the group consisting ofacrylic, acrylonitrile, polyvinylidene chloride, fluorosilicone,polyurethane, acrylonitrile butadiene rubber, fluoro polymers,hydrogenated NBR, silicone rubber coatings, styrene butadiene polymer,fluoroelastomer polymer, fluorosilicone polymer, acrylic-acrylonitrilepolymer, carboxylated acrylonitrile polymer, carboxylated styrenebutadiene polymer, chloroprene rubber polymer, ethylene propylene rubberpolymer, ethylene/vinyl acetate, epoxy, and mixtures thereof.
 36. Thegasket of claim 22 in which the coating extends a distance in the rangeof from about 5 to about 80 mils past the corner.
 37. The gasket ofclaim 22 in which the coating extends a distance in the range of fromabout 10 to about 80 mils past the corner.
 38. The gasket of claim 22 inwhich the coating extends past each face.
 39. The gasket of claim 22having a release coating on at least a portion of the gasket sheet whichhas not been coated for sealing ability.